Nga koranu konukara Te hiko a-ringa ENiCrFe-1 Ko nga taputapu Welding

Nga koranu nikareti Te hiko a-ringa ENiCrFe-1 Ko nga taputapu Welding e whakaatuhia ana

GB/T13814 ENi6062

AWS A5.11 ENiCrFe-1

A5.11M ENiCrFe-1

ISO 14172:E Ni 6062

Whatapp:+8613252436578

E-mail: sale@welding-honest.com

Waitohu:JINGLEI

Tauira:GEN-CF1（Ni307-1）

Polarity tuku hiko:DC+

Taketake:Haina

Utu mo:Nga koranu nika

Rahi:2.6*300mm 3.2*350mm 4.0*350mm

MOQ:1T Raukaha:1200T Ia marama

Utu:TT,LC

OEM:Ka taea te kaihoko

Tukuna he imeera ki a matou

Taipitopito Hua

WHAKAMAHI

Tohu Hua

KAUPAPA KAUPAPA:

KONO(wt%)	C	Mn	Si	Cr	Ni	Fe	Nb+Ta	P	S
GB/T RULES	0.08	3.50	0.80	13.0-17.0	≥62	11.00	0.5-4.0	0.02	0.015
Nga Ture AWS	0.08	3.50	0.75	13.0-17.0	≥62	11.00	1.5-4.0	0.03	0.015
UARA TAUIRA	0.048	2.97	0.34	15.6	69.6	8.94	2.65	0.050	0.007

TE KAUPAPA MAHI:

WHAI	KAUPAPA KAUPAPA(MPa)	TE KAUPAPA KAUPAPA(MPa)	WARA WHAKAMAHI J/℃	WHAKARANGA(%)
GB/T RULES	360	550	-	27
Nga Ture AWS	-	550	-	30
UARA TAUIRA	435	665	-	43

NGĀ TAWHE WELDING E WHAKATAHIngia ana:

NGĀ WHAKATAKITANGA (mm)		2.6*300	3.2*350	4.0*350
TE HIKO (Amp)	H/W	69-95	70-115	95-145
	O/W	55-80	65-110	80-130

Motuhake

He iti te momo hauwai hiko ira ringa, ko te hanganga ingoa (paerae taumaha) ko te 7ONi-15Cr-8Fe-3.5Mn-2.5Nb (Cb) +Ta, nika - chromium - rino koranu hiko.

Na te nui o te ihirangi o te koranu, ka taea te urutau ki te awhe pāmahana mai i te iti o te pāmahana ki te 980 ℃.Heoi, ka teitei ake te pāmahana i te 820 ℃, ka heke te ātete me te kaha o te hāora.

Pewa pumau, ataahua te hanga, paku pakaru, ngawari te tango para, te aukati porosity pai, he pumau nga taonga miihini o te whakarewa whakarewa.

Whakaatuhia te taipitopito

Tukunga

Mo matou

Te pupuhi wheketere tūturu

Take tono

8.2-ton te kawe nui

JU2000E papaa keri jack-up

Supercore SG

Te pupuhi wheketere tūturu

KONO(wt%)	C	Mn	Si	Cr	Ni	Fe	Nb+Ta	P	S
GB/T RULES	0.08	3.50	0.80	13.0-17.0	≥62	11.00	0.5-4.0	0.02	0.015
Nga Ture AWS	0.08	3.50	0.75	13.0-17.0	≥62	11.00	1.5-4.0	0.03	0.015
UARA TAUIRA	0.048	2.97	0.34	15.6	69.6	8.94	2.65	0.050	0.007