Kowiri tira Hiko A-ringa E316L-16 uta uta uta waea whiri waea
KAUPAPA KAUPAPA:
KONO(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
GB/T RULES | 0.04 | 0.5-2.5 | 1.00 | 17.0-20.0 | 11.0-14.0 | 2.0-3.0 | 0.04 | 0.03 | 0.75 |
Nga Ture AWS | 0.04 | 0.5-2.5 | 1.00 | 17.0-20.0 | 11.0-14.0 | 2.0-3.0 | 0.04 | 0.03 | 0.75 |
UARA TAUIRA | 0.028 | 0.095 | 0.75 | 18.8 | 11.6 | 2.4 | 0.027 | 0.003 | 0.05 |
TE KAUPAPA MAHI:
WHAI | KAUPAPA KAUPAPA(MPa) | TE KAUPAPA KAUPAPA(MPa) | WHAKAMAHI ℃xh | WARA WHAKAMAHI J/℃ | WHAKARANGA(%) | |||||
GB/T RULES | - | 490 | - | - | 25 | |||||
Nga Ture AWS | - | 490 | - | - | 30 | |||||
UARA TAUIRA | - | 575 | - | - | 39 |
NGĀ TAWHE WELDING E WHAKATAHIngia ana:
NGĀ WHAKATAKITANGA (mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
TE HIKO (Amp) | H/W | 50-75 | 70-95 | 80-120 | 110-160 | 160-190 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 |