Nga koranu konukawata A-ringa ENi-1 nga mahi hanga tito weld
KAUPAPA KAUPAPA:
| KONO(wt%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
| GB/T RULES | 0.10 | 0.75 | 1.20 | ≥92 | 0.70 | 1.0-4.0 | 0.20 | 0.02 | 0.015 |
| Nga Ture AWS | 0.10 | 0.75 | 1.25 | ≥92 | 0.75 | 1.0-4.0 | 0.25 | 0.03 | 0.02 |
| UARA TAUIRA | 0.046 | 0.06 | 0.82 | 95.5 | 0.12 | 2.7 | 0.01 | 0.007 | 0.001 |
TE KAUPAPA MAHI:
| WHAI | KAUPAPA KAUPAPA(MPa) | TE KAUPAPA KAUPAPA(MPa) | WARA WHAKAMAHI J/℃ | WHAKARANGA(%) | ||||
| GB/T RULES | 200 | 410 | - | 18 | ||||
| Nga Ture AWS | - | 410 | - | 20 | ||||
| UARA TAUIRA | 310 | 435 | - | 29 | ||||
NGĀ TAWHE WELDING E WHAKATAHIngia ana:
| NGĀ WHAKATAKITANGA (mm) | 2.6*300 | 3.2*350 | 4.0*350 | |||||||
| TE HIKO (Amp) | H/W | 65-95 | 70-115 | 95-145 | ||||||
Titanium-calcium irahiko ringa, te hanganga ingoa (ōrau ma te taumaha) ko 95Ni-2.5Ti.
Pewa pumau, ataahua te hanga, paku pakaru, ngawari te tango para, te aukati porosity pai.
He pai nga ahuatanga miihini o te konganuku kua whakauruhia, te parenga wera, te aukati waikura, te whakakotahi me te aukati kapiti.
Cr-Mo nga taonga raima whakarewa me nga taputapu hiko hiko e whakamahia ana i roto i nga taputapu parani hinu.
-
158,000 tone te waka taika Suez
Supercore SG
KAUPAPA KAUPAPA:
| KONO(wt%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
| GB/T RULES | 0.10 | 0.75 | 1.20 | ≥92 | 0.70 | 1.0-4.0 | 0.20 | 0.02 | 0.015 |
| Nga Ture AWS | 0.10 | 0.75 | 1.25 | ≥92 | 0.75 | 1.0-4.0 | 0.25 | 0.03 | 0.02 |
| UARA TAUIRA | 0.046 | 0.06 | 0.82 | 95.5 | 0.12 | 2.7 | 0.01 | 0.007 | 0.001 |
TE KAUPAPA MAHI:
| WHAI | KAUPAPA KAUPAPA(MPa) | TE KAUPAPA KAUPAPA(MPa) | WARA WHAKAMAHI J/℃ | WHAKARANGA(%) | ||||
| GB/T RULES | 200 | 410 | - | 18 | ||||
| Nga Ture AWS | - | 410 | - | 20 | ||||
| UARA TAUIRA | 310 | 435 | - | 29 | ||||
NGĀ TAWHE WELDING E WHAKATAHIngia ana:
| NGĀ WHAKATAKITANGA (mm) | 2.6*300 | 3.2*350 | 4.0*350 | |||||||
| TE HIKO (Amp) | H/W | 65-95 | 70-115 | 95-145 | ||||||
Tuhia to korero ki konei ka tukuna mai ki a matou