Nga koranu nika TIG ERNi-1 Hononga hono
KAUPAPA KAUPAPA:
| KONO(wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Ti | P | S |
| GB/T RULES | 0.15 | 1.00 | 0.70 | - | ≥92 | - | 1.0 | 2.0-3.5 | 0.03 | 0.015 |
| Nga Ture AWS | 0.15 | 1.00 | 0.75 | - | ≥93 | - | 1.0 | 2.0-3.5 | 0.03 | 0.015 |
| UARA TAUIRA | 0.005 | 0.48 | 0.26 | 0.46 | 94.69 | 0.001 | 0.07 | 2.95 | 0.001 | 0.001 |
TE KAUPAPA MAHI:
| WHAI | KAUPAPA KAUPAPA(MPa) | TE KAUPAPA KAUPAPA(MPa) | WARA WHAKAMAHI J/℃ | WHAKARANGA(%) | ||||
| GB/T RULES | - | - | - | - | ||||
| Nga Ture AWS | - | - | - | - | ||||
| UARA TAUIRA | - | 550 | 276/-196 | 36 | ||||
Waea nickel hau fehokotaki'anga parakore, hanganga ingoa ko 96%Ni-3%Ti.
Na te taapiri o te huānga Ti rawaka, ka taea te whakaheke pai i te porosity i roto i te mahi whakapiri.
Pewa pumau, ataahua te hanga, pai te rere o te rino whakarewa, me te pai o te mahi whakahiato.
-
37,000 tone te kaipuke uta uta
-
JU2000E rewa keri-ake
-
Pouaka wero haumaru
KAUPAPA KAUPAPA:
| KONO(wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Ti | P | S |
| GB/T RULES | 0.15 | 1.00 | 0.70 | - | ≥92 | - | 1.0 | 2.0-3.5 | 0.03 | 0.015 |
| Nga Ture AWS | 0.15 | 1.00 | 0.75 | - | ≥93 | - | 1.0 | 2.0-3.5 | 0.03 | 0.015 |
| UARA TAUIRA | 0.005 | 0.48 | 0.26 | 0.46 | 94.69 | 0.001 | 0.07 | 2.95 | 0.001 | 0.001 |
TE KAUPAPA MAHI:
| WHAI | KAUPAPA KAUPAPA(MPa) | TE KAUPAPA KAUPAPA(MPa) | WARA WHAKAMAHI J/℃ | WHAKARANGA(%) | ||||
| GB/T RULES | - | - | - | - | ||||
| Nga Ture AWS | - | - | - | - | ||||
| UARA TAUIRA | - | 550 | 276/-196 | 36 | ||||
-
Nga koranu nikeli Te hiko a-ringa ERNiCrMo-3(Mod) ...
-
Nga koranu nika TIG ERNiCrFe-7A Te hono honohono
-
Nga koranu konukawata A-ringa ENiCrFe-1 Weldin...
-
Nga koranu nikeli Te hiko a-ringa ENiCrFe-9 Weldin...
-
Koranu konukawata A-ringa hiko ENi-1 weld fabri...
-
Koranu nikeli te hiko hiko ENiCrMo-13 weld ...
Tuhia to korero ki konei ka tukuna mai ki a matou